2H-NbSe2 single crystal flake (ca. 2 x 2 x 0.5 mm in size) by chemical vapor transport is employed as the precursor for a top-down preparation of NbSe2 micro/nanoparticles by two kinds of processes, i.e. (1) mechanical exfoliation; (2) ultrasonic-assisted exfoliation in ethanol without ageing and with ageing for 210 days. NbSe2 micro/nanoparticles are applied on top of a Cu disk by a drop-casting process and the tribological property in sliding against a Cu pin under sliding electrical contact is investigated at room temperature. Mechanical exfoliation produces NbSe2 microplatets with typical sizes of 1 mu m to 30 mu m with a thickness less than 2 mu m. Ultrasonic-assisted exfoliation without aging facilitates the formation of NbSe2 micro/nanoplatets with sizes of 0.1 mu m to 25 mu m and nano-whiskers with 100 nm in diameter and 1 similar to 3 mu m in length, but Nb2O5 and Se are also found on the basis of XPS results. Prolonged aging of the suspensions modifies the morphology by converting platets and whiskers into corrugated floccules (hybrid material), which are composed of Nb2O5, Se, NbSe2, and graphene. Notably, NbSe2 micro/nanoparticles by ultrasonic-assisted exfoliation without ageing exhibit an excellent lubricating property with low friction coefficient (0.3), mild wear, and longer wear lifetime (120 min) than that of mechanical exfoliated NbSe2 microplatets (10 min). The wear lifetime for the aged NbSe2 micro/nanoparticles can be as long as 504 min and are 4.2 times of the sample without aging, which can be a good solid lubricant for sliding electrical contact