We developed and analyzed a novel non-sparking material based on CuAlBe for applications in potentially explosive environments. Using a master alloy of CuBe, an established material for anti-sparking tools used in oil fields, mines, or areas with potentially explosive gas accumulations, and pure Al, we used an Ar atmosphere induction furnace to obtain an alloy with ~10 wt% Al and ~2 wt% Be percentages and good chemical and structural homogeneity. The new material was tested in an explosive gaseous mixture (10% H 2 or 6.5% CH 4) under extremely strong wear for 16,000 cycles, and no hot sparks capable of igniting the environment were produced. The material was used in the form of hot-rolled plates obtained from melted ingots. The experimental results reflect the use of a suitable material for non-sparking tools. This material has good deformability during hot rolling, abnormal grain growth during deformation under heat treatment and special thermo-mechanical processing, and no high chemical composition variation. Additionally, there are slightly different corrosion resistance and mechanical properties between the melt and hot-rolled state of CuAlBe material. Through hot rolling, the material’s corrosion resistance increased, reducing the chances of generating sparks capable of causing explosions. Abstract We developed and analyzed a novel non-sparking material based on CuAlBe for applications in potentially explosive environments. Using a master alloy of CuBe, an established material for anti-sparking tools used in oil fields, mines, or areas with potentially explosive gas accumulations, and pure Al, we used an Ar atmosphere induction furnace to obtain an alloy with ~10 wt% Al and ~2 wt% Be percentages and good chemical and structural homogeneity. The new material was tested in an explosive gaseous mixture (10% H 2 or 6.5% CH 4) under extremely strong wear for 16,000 cycles, and no hot sparks capable of igniting the environment were produced. The material was used in the form of hot-rolled plates obtained from melted ingots. The experimental results reflect the use of a suitable material for non-sparking tools. This material has good deformability during hot rolling, abnormal grain growth during deformation under heat treatment and special thermo-mechanical processing, and no high chemical composition variation. Additionally, there are slightly different corrosion resistance and mechanical properties between the melt and hot-rolled state of CuAlBe material. Through hot rolling, the material’s corrosion resistance increased, reducing the chances of generating sparks capable of causing explosions. Keywords: non-sparking material; CuAlBe; microstructural and mechanical properties