During the laser-based directed energy deposition (DED-LB) processing, a WC-12Co composite coating with high hardness and strong wear resistance was successfully prepared on a 316L stainless steel substrate by adopting a high-precision coaxial powder feeding system using a spherical WC-12Co composite powder, which showed a large number of dendritic carbides and herringbone planar crystals on the substrate-binding interface. The influences of laser power on microstructural and mechanical properties (e.g., hardness, friction resistance) of WC-12Co composite surfaces were investigated. The results show that laser power has a significant effect on determining the degree of Co phase melting around the WC particles and the adhesion strength between the matrix and the coating. Lower laser power does not meet the melting requirements of WC particles, thus weakening the molding quality of the composite coating. At high laser power, it is possible to dissolve the WC particles and melt the metal powder between the particles, thus improving the material properties. The laser power increased from 700 W to 1000 W and the average hardness of the coating surface gradually increased from 1166.33 HV to 1395.70 HV, which is about 4–5 times higher than the average hardness of the substrate (about 281.76 HV). In addition, the coatings deposited at 1000 W showed better wear resistance. This work shows that the processing parameters during laser-directed energy deposition can be optimized to prepare WC-12Co composite coatings with excellent mechanical properties. Abstract During the laser-based directed energy deposition (DED-LB) processing, a WC-12Co composite coating with high hardness and strong wear resistance was successfully prepared on a 316L stainless steel substrate by adopting a high-precision coaxial powder feeding system using a spherical WC-12Co composite powder, which showed a large number of dendritic carbides and herringbone planar crystals on the substrate-binding interface. The influences of laser power on microstructural and mechanical properties (e.g., hardness, friction resistance) of WC-12Co composite surfaces were investigated. The results show that laser power has a significant effect on determining the degree of Co phase melting around the WC particles and the adhesion strength between the matrix and the coating. Lower laser power does not meet the melting requirements of WC particles, thus weakening the molding quality of the composite coating. At high laser power, it is possible to dissolve the WC particles and melt the metal powder between the particles, thus improving the material properties. The laser power increased from 700 W to 1000 W and the average hardness of the coating surface gradually increased from 1166.33 HV to 1395.70 HV, which is about 4–5 times higher than the average hardness of the substrate (about 281.76 HV). In addition, the coatings deposited at 1000 W showed better wear resistance. This work shows that the processing parameters during laser-directed energy deposition can be optimized to prepare WC-12Co composite coatings with excellent mechanical properties. Keywords: DED-LB; composite coating; wear property; laser power