The 7A04 Al alloy is a commonly used lightweight metal material; however, its low wear resistance limits its application. In this study, the wear resistance of this alloy was improved by preparing micro-arc oxidation (MAO) coatings, MAO/MoS 2 composite coatings, and hard-anodized (HA) coatings on its surface. The friction and wear behaviors of these three coatings with diamond-like coated (DLC) rings under oil lubrication conditions were investigated using a ring–block friction tester. The wear rates of the coatings on the block surfaces were determined using laser confocal microscopy, and the wear trajectories of the coatings were examined using scanning electron microscopy. The results indicated that, among the three coatings, the MAO/MoS 2 coating had the lowest coefficient of friction of 0.059, whereas the HA coating had the lowest wear rate of 1.47 × 10 −6 mm/Nm. The MAO/MoS 2 coatings exhibited excellent antifriction properties compared to the other coatings, whereas the HA coatings exhibited excellent anti-wear properties. The porous structure of the MAO coatings stored lubricant and replenished the lubrication film under oil lubrication. Meanwhile, the introduced MoS 2 enhanced the densification of the coating and functioned as a solid lubricant. The HA coating exhibited good wear resistance owing to the dense structure of the amorphous-phase aluminum oxide. The mechanisms of abrasive and adhesive wear of the coatings under oil lubrication conditions and the optimization of the tribological properties by the solid–liquid synergistic lubrication effect were investigated. This study provides an effective method for the surface modification of Al alloys with potential applications in the aerospace and automotive industries.